CL-SR-50 Polycarboxylate Superplasticizer 50% Solid Content(High Slump Retention Type)

Product ID：Polycarboxylate Superplasticizer Liquid
Phone: +86 18366819567
Email: chengli@chenglicn.com
peony@chenglicn.com
nina@chenglicn.com
vivian@chenglicn.com
jennifer@chenglicn.com

Technical Data Sheet

Appearance	Colorless to yellowish or brown viscous liquid
Bulk density(kg/m³,20℃)	1.107
Solid content(liquid)(%)	40%,50%,55%
PH value(20degree)	6~8
Alkali Content(%)	≤0.50
Sodium Sulfate Content	0.004
Chlorine content	0.0007%
Water reducing ratio	30%

Concrete Performance 50%(slump retention type)

No.	Inspection Items	Unit	Standard Value	Test Results
1	1h After Fluidity of Cement Paste	mm	≥220	240
2	Water Reducing Rate	%	≥25	30
3	Atmospheric Pressure Bleeding Rate	%	≤60	21
4	The Difference Between the Setting Time	min	Initial ＜-90	35
4	The Difference Between the Setting Time	min	Final ＜-90	20
5	Slump Variation Retention	30min	≥180	240
		60min	≥180	280
		120min	≥180	280
		180min	≥180	260
6	Ratio of Compressive Strengh	3d	≥170	180
		7d	≥150	165
		28d	≥135	145
7	Effect on Reinforcement Corrosion	/	No Corroding	No Corroding
8	Ratio of Shrinkage	/	≤110	105
Tested by Shanlv P.O.42.5 ordinary portland cement, with the dosage of 0.3% of CL-SR-50

Packaging: 200kgs/drum 1000L/IBC tank 23tons/flexitank Storage: to be stored in plastic or stainless steel container,please store dry at usual ambient temperature and protect from excessive heat(below 40℃)Shelflife: 1yearTransport regulation: not handle with care to avoide breakage when moving,keep from excessive heat.this product is non-toxic,non-irritating,non-combustible.

Technical Data Sheet

Appearance	Colorless to yellowish or brown viscous liquid
Bulk density(kg/m³,20℃)	1.107
Solid content(liquid)(%)	40%,50%,55%
PH value(20degree)	6~8
Alkali Content(%)	≤0.50
Sodium Sulfate Content	0.004
Chlorine content	0.0007%
Water reducing ratio	30%

Concrete Performance 50%(slump retention type)

No.	Inspection Items	Unit	Standard Value	Test Results
1	1h After Fluidity of Cement Paste	mm	≥220	240
2	Water Reducing Rate	%	≥25	30
3	Atmospheric Pressure Bleeding Rate	%	≤60	21
4	The Difference Between the Setting Time	min	Initial ＜-90	35
4	The Difference Between the Setting Time	min	Final ＜-90	20
5	Slump Variation Retention	30min	≥180	240
		60min	≥180	280
		120min	≥180	280
		180min	≥180	260
6	Ratio of Compressive Strengh	3d	≥170	180
		7d	≥150	165
		28d	≥135	145
7	Effect on Reinforcement Corrosion	/	No Corroding	No Corroding
8	Ratio of Shrinkage	/	≤110	105
Tested by Shanlv P.O.42.5 ordinary portland cement, with the dosage of 0.3% of CL-SR-50